Flexible Cable Issues

Started by KAVINRAJ, February 06, 2017, 12:16:34 PM

Previous topic - Next topic

KAVINRAJ




Dear All,

     Multi core Flexible  (105 deg) cable recently we manufactured,but found that that flexibility is not good,we used class 5 copper,insulation compound TI/3 & Sheathing compound TM/3.Even sheath colour also not pure white it came creamy colour,kindly advise me regarding flexibility problem and master batch percentage details.

e.arp

Check your compound shore parameter.For insulation shore should be around 90-94 shore A,for sheating 82-86 shore A.

Eoforwine SIGEWEARD

it is not related colour problem but anyway you can use EVA based compound.